Plasma enhanced metalorganic chemical vapor deposition of amorphous aluminum nitride Academic Article uri icon

abstract

  • Plasma enhanced deposition of amorphous aluminum nitride (AIN) using trimethylaluminum, hydrogen, and nitrogen was performed in a capacitively coupled plasma system. Temperature was varied from 350 to 550°C, and pressure dependence of the film structure was investigated. Films were characterized by Fourier transform infrared, Rutherford backscattering (RBS), ellipsometry, and x-ray diffraction (XRD). The films are amorphous in nature, as indicated by XRD. Variations in the refractive index were observed in ellipsometric measurements, which is explained by the incorporation of carbon in the films, and confirmed by RBS. Capacitance-voltage, conductance-voltage (G-V), and current-voltage measurements were performed to reveal bulk and interface electrical properties. The electrical properties showed marked dependence on processing conditions of the AIN films. Clear peaks as observed in the G-V characteristics indicated that the losses are predominantly due to interface states. The interface state density ranged between 1010 and 1011 eV-1 cm-2. Annealing in hydrogen resulted in lowering of interface state density values. © 2001 American Institute of Physics.

altmetric score

  • 6

author list (cited authors)

  • Harris, H., Biswas, N., Temkin, H., Gangopadhyay, S., & Strathman, M.

citation count

  • 32

publication date

  • December 2001