Mixed-dimensional nanomaterials composed of one-dimensional (1D) and two-dimensional (2D) nanomaterials, such as graphene-silver nanowire (AgNW) composite sandwiched structures, are promising candidates as building blocks for multifunctional structures and materials. However, their mechanical behavior and failure mechanism have not yet been fully understood. In this work, we have performed integrated experimental, theoretical, and numerical studies to explore the performance and failure modes of graphene-AgNW composite under tensile and impact loading conditions. In situ tensile tests using a nanoindenter, implemented with a push-to-pull device and a laser-induced projectile impact test system, are used to shed light on load-bearing mechanisms in graphene-AgNW composites. Multiple failure modes have been observed in both experimental setups and analyzed with numerical and theoretical models. Results show that in the tensile loading the distribution of AgNW, as characterized by the effective free length, is the key parameter determining the failure mode. As for the impact failure scenarios, compared with failure modes observed in pure graphene cases, the mechanical reinforcing effect of AgNW will transform the failure mode from a scattered tensile fracture along radial directions to a shear failure that is constrained in a relatively local domain. Theoretical analysis using shear lag modeling, Timoshenko plate theory, molecular dynamics modeling, and finite element modeling approaches are adopted to further establish the failure modes.