Impact of selenization with NaCl treatment on the physical properties and solar cell performance of crack-free Cu(In,Ga)Se2 microcrystal absorbers.
Academic Article
Overview
Research
Identity
Additional Document Info
Other
View All
Overview
abstract
In this study, we developed an ink using hexanethiol and Cu(In,Ga)Se2 microcrystals (CIGSe MCs) to make thin films via doctor blade coating. Besides, crack-free thin films were obtained by optimizing CIGSe MC powder concentration and annealing temperature. Subsequently, single-step selenization was performed with and without sodium chloride (NaCl) surface treatment by carefully tuning the temperature. A crack-free surface with densely packed grains was obtained at 500 C after NaCl treatment. Moreover, the structural parameters of the thin film (annealed at 350 C) were significantly modified via selenization with NaCl at 500 C. For instance, the FWHM of the prominent (112) plane reduced from 1.44 to 0.47, the dislocation density minimized from 13.10 to 1.40 1015 lines per m2, and the microstrain decreased from 4.14 to 1.35 10-3. Remarkably, these thin films exhibited a high mobility of 26.7 cm2 V-1 s-1 and a low resistivity of 0.03 cm. As a proof of concept, solar cells were engineered with a device structure of SLG/Mo/CIGSe/CdS/i-ZnO/Al-ZnO/Ag, wherein a power conversion efficiency (PCE) of 5.74% was achieved with exceptional reproducibility. Consequently, the outcomes of this investigation revealed the impact of selenization temperature and NaCl treatment on the physical properties and PCE of hexanethiol-based crack-free CIGSe MC ink-coated absorbers, providing new insights into the groundwork of cost-effective solar cells.