Preparation of diamondlike carbon films by high-intensity pulsed-ion-beam deposition
Academic Article
Overview
Research
Identity
Additional Document Info
Other
View All
Overview
abstract
Diamondlike carbon (DLC) films were prepared by high-intensity pulsed-ion-beam ablation of graphite targets. A 350 keV, 35 kA, 400 ns beam, consisting primarily of hydrogen, carbon, and oxygen ions was focused onto a graphite target at a fluence of 1545 J/cm2. Amorphous carbon films were deposited at up to 30 nm per pulse, corresponding to an instantaneous deposition rate greater than 1 mm/s. Electrical resistivities were between 1 and 1000 cm. Raman spectra indicate that diamondlike carbon is present in most of the films. Electron-energy-loss spectroscopy indicates significant amounts of sp3-bonded carbon, consistent with the presence of DLC. Scanning electron microscopy showed most films contain 100 nm features, but micron size particles were deposited as well. Initial tests revealed favorable electron field-emission behavior.