Highly Efficient Artificial Photosynthesis of Formate from CO2 and Water on Heterojunction Copper Iron Oxide Catalysts
Conference Paper
Overview
Research
Identity
Other
View All
Overview
abstract
Solar CO2 recycling has received wide attention primarily to address global CO2 emission and to convert CO2 and water to value-added chemicals. Despite a long research history over the past four decades, the technology remains in an early stage, with low CO2 conversion efficiency and selectivity. CO2 is highly stable and has limited solubility in water, and its reduction requires multiple proton-coupled electron transfers, resulting in a range of carbon intermediates (C1C3) as well as a larger amount of H2 over CO2 conversion products. For the realization of solar CO2 recycling, the system of interest should be operated sustainably, which requires the development of not only energy-efficient and cost-effective materials but also stand-alone, complete reaction processes (CO2 reduction and water oxidation) operating for long periods without any external bias. A range of semiconductors (mostly p-types) have been studied for CO2 conversion, including GaP, InP, GaAs, Si, Cu2O, and CuFeO2, all of which have narrow bandgaps (Eg) and sufficient Fermi levels (EF) capable of reducing CO2. Although promising, these aterials inherently require potential biases to drive the CO2 reduction reaction and compete with other metallic electrodes, whereas complete reactions (CO2 reduction and water oxidation) have been rarely demonstrated due to large overpotentials. Photocathode-photoanode couples have been demonstrated to operate, yet the syntheses of materials are complicated and the energy conversion efficiency is low. We have searched for high-efficiency, low-cost, and scalable p-type materials and found that CuFeO2 and CuO mixed materials meet all requirements. To our surprise, this material converted CO2 to formate with selectivity greater than 90% over 1 week and simultaneously produced molecular oxygen via water oxidation when simply wired to an inert anode (Pt foil) without any external bias under circum-neutral pH. The solar-to-formate (STF) energy efficiency was in the range of 0.71.2%, which is the highest reported value and comparable to the efficiency of photosynthesis occurring in most plants. For comparison, CuFeO2, CuO, and even Cu2O were fabricated; however, their efficiencies for formate production were much lower, and no oxygen was evolved.
name of conference
Qatar Foundation Annual Research Conference Proceedings Volume 2016 Issue 1